CuZn36Pb3

ASTM B16; SAE J461, SAE J463

  • Architecture
  • General Engineering
  • Automotive
  • Consumer Products
  • Plumbing

Typical Uses

Architecture
Terrazzo Strip

Automotive
Sensor Bodies, Thermostat Parts, Fluid Connectors, Threaded Inserts for Plastic

Builders Hardware
Lock Bodies, Fittings, Hardware

Consumer
Hot Combs (to Straighten Hair), Fasteners, Screws, Nuts, Bolts

Industrial
Faucet Components, Pinions, Automatic Screw Machine Parts, Pneumatic Fittings, Gears, Nozzles,
Valve Stems, Valve Trim, Valve Seats, Gauges, Fluid Connectors, Screw Machine Products, Adapters, Unions

Plumbing
Faucet Stems, Plumbers' Brass Goods, Faucet Seats, Plumbing Fittings

אורך מוט : 10ft – 12ft
מוטות מלבניים : W: 1/2″ – 4″
מוטות מרובעים : 3/8″ – 1.5″
מוטות משושים : 3/8″ – 2″
מוטות עגולים : 3/8″ – 3″
פרופילים : According to customers drawing
זמינות מוצר

C36000

Chemical Composition

(%max, unless shown as range or min)

Cu Fe Pb Zn
Min/Max 60.0-63.0 0.35 2.5-3.7 Rem

Note: Cu + Sum of Named Elements, 99.5% min.

Applicable Specifications

* Bar, Rod, Shapes – ASTM B16; SAE J461, SAE J463

Fabrication Processes

* Machining
* Roll Threading and Knurling

Fabrication Properties

Joining Technique Suitability
Soldering Excellent
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended
Spot Weld Not Recommended
Seam Weld Not Recommended
Butt Weld Fair
Capacity for Being Cold Worked Fair
Capacity for Being Hot Formed Fair
Machinability Rating 100

Standard Temper Designation:

* H02 – Half Hard

Mechanical Properties (ASTM B16)

Diameter or Distance Between
Parallel Surfaces, in. [mm]		 Tensile Strength, min Yield Strength, at 0.5% Extension Under Load, min Elongation(1), min, % Rockwell B Hardness(2),(3)
ksi MPa ksi MPa Round Hexagonal and Octagonal
Rod
1/2 [12] and under 57 395 25 170 7 – –
over 1/2 [12] to 1 [25] incl. 55 380 25 170 10 60 – 80 55 – 80
over 1 [25] to 2 [50] incl. 50 345 20 140 15 55 – 75 45 – 80
over 2 [50] to 3 [75] incl. 45 310 15 105 20 45 – 70 40 – 65
over 3 [75] to 4 [100] incl. 45 310 15 105 20 40 – 65 35 – 60
over 4 [100] 40 275 15 105 20 25 min 25 min
Bar
Thickness, in. [mm] Width, in. [mm]
1/2 [12] and under 1 [25] and under 50 345 25 170 10 – 45 – 85
1/2 [12] and under over 1 [25] to 6 [150] 45 310 17 115 15 – 35 – 70
over 1/2 [12] to 2 [50] incl. 2 [50] and under 45 310 17 115 15 – 40 – 80
over 1/2 [12] to 2 [50] incl. over 2 [50] to 6 [150] 40 275 15 105 20 – 35 – 70
over 2 [50] over 2 [50] to 4 [100] 40 275 15 105 20 – 35 – 70

(1) In any case, a minimum gage length of 1 in. [25mm] shall be used. SI elongation values are based on a gage length of 5.65 times the square root of the area for dimentions greater than 2.5 mm.
(2) Determined on the cross section midway between surface and center.
(3) Rockwell hardness requirements are not established for diameters less than 1/2 in. [12 mm].

Physical Properties

US Customary Metric
Melting Point – Liquidus 1650 F 900 C
Melting Point – Solidus 1630 F 885 C
Density 0.307 lb/in3 at 68 F 8.5 gm/cm3 at 20 C
Specific Gravity 8.5 8.5
Electrical Resistivity 39.9 ohms-cmil/ft at 68 F 6.63 microhm-cm at 20 C
Electrical Conductivity 26 %IACS at 68 F 0.152 MegaSiemens/cm at 20 C
Thermal Conductivity 67.0 Btu · ft/(hr · ft2·°F) at 68 F 116.0 W/m ·°K at 20 C
Coefficient of Thermal Expansion 11.4·10-6 per °F (68-572 F) 20.5·10-6 per °C (20-300 C)
Specific Heat Capacity 0.09 Btu/lb/°F at 68 F 377 J/kg · °K at 20 C
Modulus of Elasticity in Tension 14000 ksi 97000 MPa
Modulus of Rigidity 5300 ksi 37000 MPa