CuAl10Fe2-C

EN1982

Similar alloyes:  CuAl10Fe2-C; AB1-C

  • Automotive
  • Industrial Machinery
  • Marine
  • Oil & Gas

Typical Uses
Automotive, Weld Guns,Fasteners, Nuts, Large Hold Down Screws, Industrial,Pickling Hooks, Bearings, Pawl, Worm Gears, Machine Parts, Spur Gears, Heavily Loaded Worm Gears, Pump, Parts, Landing Gear Parts, Valve Bodies, Valve Guides, Valve Seats, Bearing Segments for the Steel Industrial, Pressure Blocks for the Steel Industry, High Strength Clamps, Bushings, Valves, Gears, Marine, Ship Building, Covers for Marine, Hardware Ordnance Government Fitting

Bar Length : 3000mm
Bars carrés : Up to 153mm
Barres creuses : 42X18mm – 293X237mm
Solides ronde : 32mm – 303mm
Bars & rectangle plat : Up to 303mm W
La disponibilité des produits

CC331G

Chemical Composition

(%max, unless shown as range or min)

Cu Al Fe Mn Ni Mg Pb Si Sn Zn
Min/Max 83.0-89.5 8.5-10.5 1.5-3.5 1.0 1.5 0.05 0.1 0.2 0.2 0.5

Applicable Specifications

*BS EN 1982

Fabrication Processes

* Continuous Casting

Fabrication Properties

Joining Technique Suitability
Soldering Good
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Good
Coated Metal Arc Welding Good
Machinability Rating 60

Mechanical Properties

Tensile Strength
Rm N/mm2 min.		 0.2% Proof Strength  Rp0.2 N/mm2 min. Elongation A % min. Hardness HB min.
550 200 15 130

Physical Properties

US Customary Metric
Melting Point – Liquidus 1900 F 1038 C
Melting Point – Solidus 1880 F 1027 C
Density 0.269 lb/in3 at 68 F 7.45 gm/cm3 at 20 C
Specific Gravity 7.45 7.45
Electrical Resistivity 80.2 ohms-cmil/ft at 68 F 13.33 microhm-cm at 20 C
Electrical Conductivity 13 %IACS at 68 F 0.075 MegaSiemens/cm at 20 C
Thermal Conductivity 33.9 Btu · ft/(hr · ft2·°F) at 68 F 58.7 W/m ·°K at 20 C
Coefficient of Thermal Expansion 9.0·10-6 per °F (68-572 F) 16.2·10-6 per °C (20-300 C)
Specific Heat Capacity 0.1 Btu/lb/°F at 68 F 419.0 J/kg · °K at 20 C
Modulus of Elasticity in Tension 15500 ksi 107000 MPa
Magnetic Permeability* 1.2 1.2
Magnetic Permeability** 1.27 1.27

* TQ 50 Temper, Field Strength 16 kA/m
** As Cast, Field Strength 16 kA/m