Demander d’ information

CuAl10Fe5Ni5-C

EN1982

Similar alloyes: CUAL10NI5FE5; AB2

  • Automotive
  • Industrial Machinery
  • Marin
  • Oil & Gas

Typical Uses

Builders Hardware, Window Hardware, Consumer Piano Keys, Musical Instruments

Electrical
Electrical Hardware, Fasteners, Stuffing Box Nuts Industrial Pickling Equipment, Valve Guides, Piston Guides, Valve Seats, Pump Fluid Ends, Glands, Worms, Worms Wheels, Hot Mill Guides, Hand Gun Recoil Mechanisms, Landing Gear Parts, Air Craft Components, Wear Plates, Welding Jaws, Landing Gear Parts, Glass Molds, Machine Parts, Sewage Treatment Applications, Valve Components, Bearings, Bushings, Valve Bodies, Gears

Marine
Marine Applications, Covers for Marine Hardware, Ship Building, Marine Hardware Ordnance Government Fittings

Bars carrés : Up to 153mm
Barres creuses : 42X18mm – 293X237mm
Solides ronde : 32mm – 303mm
Bars & rectangle plat : Up to 303mm W
Bar Length : 3000mm
La disponibilité des produits

CC333G

Chemical Composition

(%max, unless shown as range or min)

Cu Al Fe Mn Ni Bi Cr Mg Pb Si Sn Zn
Min/Max 76.0-83.0 8.5-10.5 4.0-5.5 3.0 4.0-6.0 0.01 0.05 0.05 0.03 0.1 0.1 0.5

Applicable Specifications

*BS EN 1982

Fabrication Processes

* Continuous Casting

Fabrication Properties

Joining Technique Suitability
Soldering Good
Brazing Fair
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Good
Coated Metal Arc Welding Good
Machinability Rating 50

Mechanical Properties

Tensile Strength
Rm N/mm2 min.		 0.2% Proof Strength
Rp0.2 N/mm2 min.		 Elongation A % min. Hardness HB min.
650 280 13 150

Physical Properties

US Customary Metric
Melting Point – Liquidus 1930 F 1054 C
Melting Point – Solidus 1900 F 1038 C
Density 0.272 lb/in3 at 68 F 7.53 gm/cm3 at 20 C
Specific Gravity 7.53 7.53
Electrical Resistivity 122.8 ohms-cmil/ft at 68 F 20.41 microhm-cm at 20 C
Electrical Conductivity 8 %IACS at 68 F 0.049 MegaSiemens/cm at 20 C
Thermal Conductivity 24.2 Btu · ft/(hr · ft2·°F) at 68 F 41.9 W/m ·°K at 20 C
Coefficient of Thermal Expansion 9.0·10-6 per °F (68-572 F) 16.2·10-6 per °C (20-300 C)
Specific Heat Capacity 0.1 Btu/lb/°F at 68 F 419.0 J/kg · °K at 20 C
Modulus of Elasticity in Tension 16000 ksi 110000 MPa
Magnetic Permeability* 1.2 1.2
Magnetic Permeability** 1.32 1.32
Poisson’s Ratio 0.32 0.32