Demander d’ information




  • General Engineering

Typical Uses

This material has proved its value in sliding bearings and withstands moderate bearing pressures very well with adequate lubrication. Especially in the engineering industry, can be manufactured economically from this material. The unique composition results in good wear and running properties, as well as good relief of end pressures and excessive stresses from inadequate or occasional interruptions of lubrication. The surface finish and hardness requirements for the opposing material are not so great as with hightin bronzes. With good lubrication, unhardened shafts can be used. The alloy has good sliding and emergency running properties


Solides ronde : 10mm-303mm
Barres creuses : 26X14mm – 292X238mm
Bars hexagonales : Up to 76mm
Bars carrés : Up to 153mm
Bars & rectangle plat : Up to 303mm W
Bar Length : 3000mm
La disponibilité des produits

CC482K- CuSn11Pb2

Chemical Composition

Cu* Al Sb Mn Fe Pb Ni P Si S Sn Zn
Min/Max 83.5-87.0 0.01 0.2 0.2 0.20 0.7-2.5 2.0 0.40 0.01 0.08 10.5-12.5 2.0

Applicable Specifications

* EN1982

Fabrication Processes

Joining Technique Suitability
Soldering Excellent
Brazing Good
Oxyacetylene Welding Fair
Gas Shielded Arc Welding Fair
Coated Metal Arc Welding Fair
Machinability Rating 20

Mechanical Properties (EN1982)

Tensile Strength, minA Yield Strength, at 0.5% Extension Under Load, minA Elongation in 2 in.
or 50 mm, min, %
ksi MPa ksi MPa
40 276 25 172 10

A Minimum tensile strength and yield strength shall be reduced 10% for cast bars having a cross section, thickness, diameter, or wall of 4 in. (102 mm) or more. The cross sections are the diameter of a round solid, the distance across the flats of a solid hexagon, the thickness of a rectangle, and the wall thickness of a tube.

Physical Properties

US Customary Metric
Melting Point – Liquidus 1830 F 999 C
Melting Point – Solidus 1528 F 831 C
Density 0.317 lb/in3 at 68 F 8.77 gm/cm3 at 20 C
Specific Gravity 8.77 8.77
Electrical Resistivity 107.4 ohms-cmil/ft at 68 F 17.86 microhm-cm at 20 C
Electrical Conductivity 10 %IACS at 68 F 0.056 MegaSiemens/cm at 20 C
Thermal Conductivity 40.8 Btu · ft/(hr · ft2·°F) at 68 F 70.6 W/m ·°K at 20 C
Coefficient of Thermal Expansion 10.2·10-6 per °F (68-392 F) 18.4·10-6 per °C (20-200 C)
Specific Heat Capacity 0.09 Btu/lb/°F at 68 F 377.1 J/kg · °K at 20 C
Modulus of Elasticity in Tension 15000 ksi 103400 MPa
Magnetic Permeability 1.0 1.0