CuZn40Pb2

CuZn40Pb2

EN 12164, EN 12165, EN 12167

  • Architecture
  • Electricity
  • General Engineering
  • Plumbing

Typical Uses

Architecture
Door Handles, Decorative Knobs, Furniture Hardware

General Engineering
Valve Bodies for Refrigeration, Chemicals

Consumer
Golf Putters, Valve Bodies for Scuba & Propane Spray Tanks, Valve Bodies for Agricultural Spray Tanks

Electrical
Covers, Fuse Bodies

Industrial
Valve Components, Forgings and Pressings of All Kinds

Bar Length : 3000mm
Bars & rectangle plat : W: 10mm – 102mm
Bars carrés : 10mm – 40mm
Bars hexagonales : 10mm – 55mm
Solides ronde : 10mm – 80mm
Profils : According to customers drawing
La disponibilité des produits

CW617N

Chemical Composition

(%max, unless shown as range or min)

Cu Al Fe Ni Pb Sn Zn Others total
Min/Max 57.0 – 59.0 0.05 0.3 0.3 1.6 – 2.5 0.3 Rem 0.2

Applicable Specifications

*BS EN 12164, BS EN 12165, BS EN 12167

Fabrication Processes

* Hot Forging and Pressing
* Hot Heading and Upsetting
* Machining

Fabrication Properties

Joining Technique Suitability
Soldering Excellent
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended
Spot Weld Not Recommended
Seam Weld Not Recommended
Butt Weld Fair
Capacity for Being Cold Worked Poor
Capacity for Being Hot Formed Excellent
Forgeability Rating 100
Machinability Rating 80

Mechanical Properties (BS EN 12165)

Material Condition Nominal Cross-Sectional Dimension Tensile
Strength
Rm
N/mm2
approx.		 0.2% Proof
Strength
Rp0.2
N/mm2
approx.		 Elongation
A
%approx.		 Hardness
HBmin.
Diameter (mm)
From Up to and including
M All As Manufactured
H080 6 80 (350) (140) (15) 80

Physical Properties

US Customary Metric
Melting Point – Liquidus 1640 F 893 C
Melting Point – Solidus 1620 F 882 C
Density 0.305 lb/in3 at 68 F 8.44 gm/cm3 at 20 C
Specific Gravity 8.44 8.44
Electrical Resistivity 38.4 ohms-cmil/ft at 68 F 6.38 microhm-cm at 20 C
Electrical Conductivity 27 %IACS at 68 F 0.158 MegaSiemens/cm at 20 C
Thermal Conductivity 69.0 Btu · ft/(hr · ft2·°F) at 68 F 119.4 W/m ·°K at 20 C
Coefficient of Thermal Expansion 11.5·10-6 per °F (68-572 F) 20.7·10-6 per °C (20-300 C)
Specific Heat Capacity 0.09 Btu/lb/°F at 68 F 377.1 J/kg · °K at 20 C
Modulus of Elasticity in Tension 15000 ksi 103400 MPa
Modulus of Rigidity 5600 ksi 38610 MPa