This material has proved its value in sliding bearings and withstands moderate bearing pressures very well with adequate lubrication. Especially in the engineering industry, can be manufactured economically from this material. The unique composition results in good wear and running properties, as well as good relief of end pressures and excessive stresses from inadequate or occasional interruptions of lubrication. The surface finish and hardness requirements for the opposing material are not so great as with hightin bronzes. With good lubrication, unhardened shafts can be used. The alloy has good sliding and emergency running properties
Bar Length :
3000mm
Bars & rectangle plat :
Up to 303mm W
Bars carrés :
Up to 153mm
Bars hexagonales :
Up to 76mm
Barres creuses :
26X14mm – 292X238mm
Solides ronde :
10mm-303mm
La disponibilité des produits
CC481K- CuSn11P
Chemical Composition
Cu*
Al
Sb
Mn
Fe
Pb
Ni
P
Si
S
Sn
Zn
Min/Max
87.0-89.5
0.01
0.05
0.05
0.10
0.25
0.10
0.6-1.0
0.01
0.05
10.0-11.5
0.05
Applicable Specifications
* EN1982
Fabrication Processes
Joining Technique
Suitability
Soldering
Excellent
Brazing
Good
Oxyacetylene Welding
Fair
Gas Shielded Arc Welding
Fair
Coated Metal Arc Welding
Fair
Machinability Rating
20
Mechanical Properties (EN1982)
Tensile Strength, minA
Yield Strength, at 0.5% Extension Under Load, minA
Elongation in 2 in.
or 50 mm, min, %
ksi
MPa
ksi
MPa
40
276
25
172
10
A Minimum tensile strength and yield strength shall be reduced 10% for cast bars having a cross section, thickness, diameter, or wall of 4 in. (102 mm) or more. The cross sections are the diameter of a round solid, the distance across the flats of a solid hexagon, the thickness of a rectangle, and the wall thickness of a tube.