CuAl10Ni5Fe4

CuAl10Ni5Fe4

EN 12163, EN 12165, EN 12167

  • Aerospace
  • Plumbing
  • Marin
  • Industrial

Typical Uses

Industrial
Hydraulic Bushings for Earth Moving Equipment, Corrosion Resistant Articles, Bushings, Bearings, Heat Exchanger Flanges, Heat Exchanger Headers, Tanks, Valve Balls, Structural Members, Pump Shafts, Aircraft Parts, Valve Guides, Plunger Tips, Welded Piping Systems, Balls, Gears, Cams, Pump Parts, Shafting, Condenser Tube for Power Stations and Desalting Units, Valve Seats

Marine
Pump Parts, Bolts, Nuts, Propellers, Ship Propellers

Plumbing
Faucets

Solides ronde : 12mm – 100mm
Bars & rectangle plat : Up to 102mm W
Bars hexagonales : 10mm – 55mm
Bars carrés : 20mm – 90mm
Bar Length : 3000mm
La disponibilité des produits

CW307G

Chemical Composition

(%max, unless shown as range or min)

Cu Al Fe Mn Ni Pb Si Sn Zn Others Total
Min/Max Rem 8.5 – 11.0 3.0 – 5.0 1.0 4.0 – 6.0 0.05 0.2 0.1 0.4 0.2

Applicable Specifications

*BS EN 12163, BS EN 12165, BS EN 12167

Fabrication Processes

* Forging
* Hot Forming

Fabrication Properties

Joining Technique Suitability
Soldering Not Recommended
Brazing Fair
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Good
Coated Metal Arc Welding Good
Spot Weld Good
Seam Weld Good
Butt Weld Good
Capacity for Being Cold Worked Poor
Capacity for Being Hot Formed Good
Forgeability Rating 75
Machinability Rating 30

Mechanical Properties

Material Condition Nominal Diameter or
Width Across-Flats (mm)		 Tensile
Strength
Rm
N/mm2
min.		 0.2% Proof
Strength
Rp0.2
N/mm2
approx.		 Elongation
A % min.		 Hardness HB
From Up to and including min. max.
M 10 80 As Manufactured
R680 10 80 680 (480) 10 — —
H170 10 80 — — — 170 210
R740 10 80 740 (530) 8 — —
H200 10 80 — — — 200 —

Rectangle (BS EN 12167)

Material Condition Rectangular bar thickness (mm) Tensile
Strength
Rm
N/mm2
min.		 0.2% Proof
Strength
Rp0.2
N/mm2
approx.		 Elongation
A % approx.		 Hardness
HB min.
Over Up to and
Including
M All As Munufactured
R700 — 6 700 (450) (10) —
H180 — 6 — — — 180
R600 6 60 600 (350) (12) —
H160 6 60 — — — 160

Physical Properties

US Customary Metric
Melting Point – Liquidus 1930 F 1054 C
Melting Point – Solidus 1895 F 1035 C
Density 0.274 lb/in3 at 68 F 7.58 gm/cm3 at 20 C
Specific Gravity 7.58 7.58
Electrical Resistivity 116.0 ohms-cmil/ft at 68 F 19.28 microhm-cm at 20 C
Electrical Conductivity 7 %IACS at 68 F 0.041 MegaSiemens/cm at 20 C
Thermal Conductivity 22.6 Btu · ft/(hr · ft2·°F) at 68 F 39.1 W/m ·°K at 20 C
Coefficient of Thermal Expansion 9.0·10-6 per °F (68-572 F) 16.2·10-6 per °C (20-300 C)
Specific Heat Capacity 0.09 Btu/lb/°F at 68 F 377.1 J/kg · °K at 20 C
Modulus of Elasticity in Tension 17500 ksi 121000 MPa
Modulus of Rigidity 6400 ksi 44130 MPa