CuAl7Si2
ASTM B 150-12 HR50, ASTM B 124-14a, SAE AMS 4634B, QQC-465B AM1
- Automotive
- Electrical
- Fasteners
- Marine
Typical Uses
Request a Quote
Round :
|
1/2" - 4" |
Bar Length :
|
10ft - 12ft |
Hexagonal :
|
1/2" - 2" |
Square :
|
1/2" - 3" |
Rectangle :
|
up to 4" |
Product availabillity
C-64200
Chemical Composition
(%max, unless shown as range or min)
|
Cu* |
Al |
Fe |
Mn |
Ni** |
Si |
Sn |
Zn |
Pb |
|
|
Min/Max |
Rem |
6.3-7.6 |
0.030 |
0.10 |
0.25 |
1.5-2.2 |
0.20 |
0.50 |
0.05 |
* Cu value includes Ag.
** Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.
Applicable Specifications
* Bar, Rod – ASTM B150
* AMS 4640
* SAE J461
* SAE J463
Fabrication Processes
* Forging
* Hot Forming
Standard Temper Designation:
* Bar, Rod – HR50 – Drawn and Stress Relieved
* Shapes – M30 – As Hot Extruded; O30 – Hot Extruded and Annealed
Fabrication Properties
| Joining Technique | Suitability |
| Soldering | Not Recommended |
| Brazing | Fair |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Spot Weld | Good |
| Seam Weld | Good |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Formed | Good |
| Forgeability Rating | 75 |
| Machinability Rating | 30 |
Mechanical Properties (ASTM B150)
|
Form
|
Diameter or Distance Between Parallel Surfaces, in. [mm]
|
Tensile Strength, min
|
Yield Strength, at 0.5% Extension Under Load, min |
Elongation in 4xdiameter or 4xthickness, min, %
|
||
|
ksi |
MPa |
ksi |
MPa |
|||
|
Shapes |
All Sizes |
85 |
585 |
42.5 |
295 |
10 |
|
Rod and Bar |
1/2 [12.7] to 1 [25.4] incl. |
110 |
760 |
68 |
470 |
10 |
|
over 1 [25.4] to 2 [50.8] incl. |
110 |
760 |
60 |
415 |
10 |
|
|
over 2 [50.8] to 3 [76.2] incl. |
105 |
725 |
55 |
380 |
10 |
|
Physical Properties
| US Customary | Metric | |
| Melting Point – Liquidus | 1930 F | 1054 C |
| Melting Point – Solidus | 1895 F | 1035 C |
| Density | 0.274 lb/in3 at 68 F | 7.58 gm/cm3 at 20 C |
| Specific Gravity | 7.58 | 7.58 |
| Electrical Resistivity | 116 ohms-cmil/ft at 68 F | 19.28 microhm-cm at 20 C |
| Electrical Conductivity | 7 %IACS at 68 F | 0.041 MegaSiemens/cm at 20 C |
| Thermal Conductivity | 22.6 Btu · ft/(hr · ft2·°F) at 68 F | 39.1 W/m ·°K at 20 C |
| Coefficient of Thermal Expansion | 9·10-6 per °F (68-572 F) | 16.2·10-6 per °C (20-300 C) |
| Specific Heat Capacity | 0.09 Btu/lb/°F at 68 F | 377.1 J/kg · °K at 20 C |
| Modulus of Elasticity in Tension | 17500 ksi | 121000 MPa |
| Modulus of Rigidity | 6400 ksi | 44130 MPa |