בקשה להצעת מחיר

SAE64

ASTM B505

  • Industrial
  • Marine
  • Fasteners

Typical Uses

Industrial Crank Shafts, Bearings, Bearing Plates, Machine Parts, Bushings, Applications Requiring Acid Resistance to Sulphite Fluids, Parts for Steel Mill Maintenance, Slide Guides for Steel Mills, High Speed, Heavy Load Bearings, Pumps, Pressure Tight Castings, Impellers, Corrosion Resistant Castings, Bushings for High Speed and Heavy Pressure.Marine Large Bearings for Ships, Builders Hardware Brackets, Fasteners Washers for Engines, Nuts

אורך מוט : 10ft – 12ft
מוטות מרובעים : up to 5”
מוטות חלולים : 1/2″X1″ – 10 1/2″X11 1/2″
מוטות עגולים : 1/2″ – 11 3/4″
מוטות משושים : up to 3”
מוטות מלבניים : up to 11” W
זמינות מוצר

C93700

Chemical Composition

(%max, unless shown as range or min)

Cu

AI

Sb

Fe

Ni

Pb

Si

S

Sn

Zn

p
Min/Max 79.0-82.0 0.005 0.50 0.70 0.50 8.0-11.0 0.005 0.08 9.0-11.0 0.8 1.5

Note: Cu + Sum of Named Elements, 99.0% min.

Applicable Specifications

* ASTM B505; SAE64

 Fabrication Processes

* Continuous Casting

Fabrication Properties

Joining Technique Suitabillity
Soldering Good
Brazing Good
Oxyacetylene Welding Not recommended
Gas Shielded Arc Welding Not recommended
Coated Metal Arc Welding Not recommended
Machinabillity 80

 Mechanical Properties (ASTM B505)

Tensile Strength, minA Yield Strength, at 0.5% Extension Under Load, minA Elongation in 2 in.
or 50 mm, min, %
ksi MPa ksi MPa
35  241 20  138 6

* Minimum tensile strength and yield strength shall be reduced 10% for cast bars having a cross section, thickness, diameter, or wall of 4 in. (102 mm) or more. The cross sections are the diameter of a round solid, the distance across the flats of a solid hexagon, the thickness of a rectangle, and the wall thickness of a tube.

Physical Properties

US Customary Metric
Melting Point – Liquidus 1705 F 929 C
Melting Point – Solidus 1403 F 762 C
Incipient Melting  600 F  316 C
Density 0.320 lb/in3 at 68 F 8.86 gm/cm3 at 20 C
Specific Gravity 8.86 8.86
Electrical Conductivity 10 %IACS at 68 F 0.059 MegaSiemens/cm at 20 C
Thermal Conductivity 27.1 Btu · ft/(hr · ft2·°F) at 68 F 46.9 W/m ·°K at 20 C
Coefficient of Thermal Expansion 10.3·10-6 per °F (68-212 F) 18.5·10-6 per °C (20-100 C)
Specific Heat Capacity 0.09 Btu/lb/°F at 68 F 377.1 J/kg · °K at 20 C
Modulus of Elasticity in Tension 11000 ksi 75800 MPa
Magnetic Permeability 1 1.0